高耐熱ABS LG化學XR-409H 耐溫116度 abs塑膠原料
產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 流動系數(shù) | 200℃，5kg | ASTM D-1238(G) | 0.3 | g/10min |
| 流動系數(shù) | 220℃,10kg | ASTM D-1238(G) | 3.0 | g/10min | |
| 流動系數(shù) | 230℃,3.8kg | ASTM D-1238(I) | 1.2 | g/10min | |
| 物理性能 | 比重 | ASTM D-792 | 1.05 | ||
| 成型收縮率 | ASTM D-955 | 0.4-0.7 | % | ||
| 機械性能 | IZOD缺口沖擊強度 | 1/8",30℃ | ASTM D-256 | 6(59)(1.1) | kg.cm/cm(J/m)(ft-lb/in) |
| 伸張率(抗拒點) | 50mm/min | ASTM D-638 | >6 | % | |
| IZOD缺口沖擊強度 | 1/4",30℃ | ASTM D-256 | 5(49)(0.9) | kg.cm/cm(J/m)(ft-lb/in) | |
| IZOD缺口沖擊強度 | 1/4",23℃ | ASTM D-256 | 13(127)(2.4) | kg.cm/cm(J/m)(ft-lb/in) | |
| 張力模數(shù) | 1mm/min | ASTM D-638 | 22700(2220)(322000) | kg/cm2(MPa)(lb/in2) | |
| 洛氏硬度 | ASTM D-955 | 108 | R Scale | ||
| 彎曲模數(shù) | 15mm/min | ASTM D-790 | 24900(2440)(354000) | kg/cm2(MPa)(lb/in2) | |
| IZOD缺口沖擊強度 | 1/8",23℃ | ASTM D-256 | 14(140)(2.6) | kg.cm/cm(J/m)(ft-lb/in) | |
| 彎曲強度 | 15mm/min | ASTM D-790 | 760(75)(10800) | kg/cm2(MPa)(lb/in2) | |
| 伸張率(破斷點) | 50mm/min | ASTM D-638 | 20 | % | |
| 張力強度 | 50mm/min | ASTM D-638 | 450(44)(6400) | kg/cm2(MPa)(lb/in2) | |
| 熱性能 | 燃燒性 | 1/10" | UL 94 | HB | class |
| 燃燒性 | 1/8" | UL 94 | HB | class | |
| 維卡軟化點 | 1kg,120℃/h | ASTM D-1525 | 135(275) | ℃(℉) | |
| 熱變形溫度 | 18.5kg/cm2,1/4"未退火 | ASTM D-648 | 107(225) | ℃(℉) | |
| 維卡軟化點 | 5kg,50℃/h | ASTM D-1525 | 116(241) | ℃(℉) | |
| 燃燒性 | 1/8" | IEC 707 | FH3-34 | mm/min | |
| 燃燒性 | 1/16" | IEC 707 | FH3-34 | mm/min | |
| 熱變形溫度 | 4.6kg/cm2,1/4"未退火 | ASTM D-618 | 116(241) | ℃(℉) | |
| 熱變形溫度 | 18.5kg/cm2,1/4"退火 | ASTM D-648 | 112(234) | ℃(℉) | |
| 熱變形溫度 | 4.6kg/cm2,1/4"退火 | ASTM D-648 | 119(245) | ℃(℉) | |