耐磨PC 日本帝人LS-2250 工程配件原料
產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | ||
| 基本性能 | 吸水率 | 24hr in 23℃ | ASTM D-570 | 0.17 | % | |
| 物理性能 | 透光率 | 3mm thick | ASTM D-1003 | Translucent | % | |
| 比重 | JIS K-7112 | 1.26 | ||||
| 阻燃性 | 1.5mm | UL 94 | V-2 | |||
| 機械性能 | 拉伸模量 | ASTM D-638 | 2300(23500) | Mpa(kgf/cm2) | ||
| 洛氏硬度 | ASTM D-785 | 67 | M標度 | |||
| 拉伸強度 | 屈服點 | ASTM D-638 | 55(560) | Mpa(kgf/cm2) | ||
| 斷裂點 | ASTM D-638 | 51(520) | Mpa(kgf/cm2) | |||
| 耐沖擊強度值 | 艾氏、帶缺口厚度3.2mm | ASTM D-256 | 290(30) | J/m(kgf·cm/cm) | ||
| 耐沖擊強度值 | 艾氏、帶缺口厚度6.4mm | ASTM D-256 | 120(12) | J/m(kgf·cm/cm) | ||
| 壓縮強度 | ASTM D-695 | 73(740) | Mpa(kgf/cm2) | |||
| 拉伸率 | 屈服點 | ASTM D-638 | 78(800) | % | ||
| 斷裂點 | ASTM D-638 | 2110(21500) | % | |||
| 電氣性能 | 耐導電徑跡性（CTI） | IEC 112 | 340 | V | ||
| 介電正切 | 60Hz | ASTM D-150 | 0.0008 | |||
| 介電率 | 60Hz | ASTM D-150 | 2.85 | |||
| 體積電阻率 | ASTM D-257 | 3×1016 | Ω.cm | |||
| 介電正切 | 106Hz | ASTM D-150 | 0.008 | |||
| 絕緣破壞強度 | 快速加壓值厚度1.6mm | ASTM D-149 | 30 | kv/mm | ||
| 介電率 | 106Hz | ASTM D-150 | 2.8 | |||
| 耐電弧性 | ASTM D-495 | 100 | sec | |||
| 加工性能 | 成型收縮率 | 流動方向 | ASTM D-955 | 0.5～0.7 | % | |
| 垂直方向 | ASTM D-955 | 0.5～0.7 | % | |||
| 熱性能 | 負荷撓曲溫度 | 負荷1.813MPa(18.6kgf/cm2) | JIS K-7207 | 136 | ℃ | |
| 溫度指數(shù) | 電學式 | 厚度1.47mm | UL 746B | 115 | °C | |
| 沖擊式 | 厚度1.47mm | UL 746B | 105 | °C | ||
| 非沖擊式 | 厚度1.47mm | UL 746B | 105 | °C | ||
| 負荷撓曲溫度 | 負荷0.451MPa(4.6kgf/cm2) | JIS K-7207 | 145 | ℃ | ||
| 線膨脹系數(shù) | 流動方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ | ||
| 垂直方向 | ASTM D-696 | 7 | 10-5cm/cm/℃ | |||