DuPont Performance Polymers Zytel® 135F NC010 Nylon 66 (Unverified Data**) 物性表
物理性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
---|---|---|---|
密度 | 1.01 g/cc | 0.0365 lb/in³ | |
1.14 g/cc | 0.0412 lb/in³ | DAM; ISO 1183 | |
吸水率 | 8.5 %
@Thickness 2.00 mm
|
8.5 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
水分吸收 | 2.70 %
@Thickness 2.00 mm
|
2.70 %
@Thickness 0.0787 in
|
DAM; Sim. to ISO 62 |
粘度 | 64000 cP
@Shear Rate 5000 1/s, Temperature 315 °C
|
64000 cP
@Shear Rate 5000 1/s, Temperature 599 °F
|
ISO 11403-1 -2 |
83000 cP
@Shear Rate 5000 1/s, Temperature 295 °C
|
83000 cP
@Shear Rate 5000 1/s, Temperature 563 °F
|
ISO 11403-1 -2 | |
105000 cP
@Shear Rate 5000 1/s, Temperature 275 °C
|
105000 cP
@Shear Rate 5000 1/s, Temperature 527 °F
|
ISO 11403-1 -2 | |
134000 cP
@Shear Rate 500 1/s, Temperature 315 °C
|
134000 cP
@Shear Rate 500 1/s, Temperature 599 °F
|
ISO 11403-1 -2 | |
195000 cP
@Shear Rate 500 1/s, Temperature 295 °C
|
195000 cP
@Shear Rate 500 1/s, Temperature 563 °F
|
ISO 11403-1 -2 | |
284000 cP
@Shear Rate 500 1/s, Temperature 275 °C
|
284000 cP
@Shear Rate 500 1/s, Temperature 527 °F
|
ISO 11403-1 -2 | |
粘度測試 | 150 cm³/g | 150 cm³/g | DAM; ISO 307 1157 1628 |
線性成型收縮率,Flow | 0.0070 cm/cm | 0.0070 in/in | DAM; ISO 294-4 2577 |
線性成型收縮率,橫向 | 0.013 cm/cm | 0.013 in/in | DAM; ISO 294-4 2577 |
機械性能 | 額定值 (公制) | 額定值 (英制) | 測試方法 |
---|---|---|---|
洛氏硬度(M 級) | 64 | 64 | 50%RH; ISO 2039-2 |
87 | 87 | DAM; ISO 2039-2 | |
洛氏硬度(R 級) | 116 | 116 | 50%RH; ISO 2039-2 |
123 | 123 | DAM; ISO 2039-2 | |
抗張強度 | 7.47 MPa
@Strain 0.960 %, Temperature 90.0 °C
|
1080 psi
@Strain 0.960 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 |
11.4 MPa
@Strain 0.480 %, Temperature 40.0 °C
|
1650 psi
@Strain 0.480 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
17.8 MPa
@Strain 2.40 %, Temperature 90.0 °C
|
2580 psi
@Strain 2.40 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
18.0 MPa
@Strain 0.480 %, Temperature 23.0 °C
|
2610 psi
@Strain 0.480 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
22.8 MPa
@Strain 0.550 %, Temperature 0.000 °C
|
3310 psi
@Strain 0.550 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
24.5 MPa
@Strain 3.84 %, Temperature 90.0 °C
|
3550 psi
@Strain 3.84 %, Temperature 194 °F
|
DAM; ISO 11403-1 -2 | |
26.5 MPa
@Strain 0.630 %, Temperature -20.0 °C
|
3840 psi
@Strain 0.630 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
41.6 MPa
@Strain 1.92 %, Temperature 40.0 °C
|
6030 psi
@Strain 1.92 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
60.5 MPa
@Strain 3.36 %, Temperature 40.0 °C
|
8770 psi
@Strain 3.36 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
65.5 MPa
@Strain 1.92 %, Temperature 23.0 °C
|
9500 psi
@Strain 1.92 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
65.7 MPa
@Strain 4.80 %, Temperature 40.0 °C
|
9530 psi
@Strain 4.80 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
82.7 MPa
@Strain 2.20 %, Temperature 0.000 °C
|
12000 psi
@Strain 2.20 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
92.9 MPa
@Strain 3.36 %, Temperature 23.0 °C
|
13500 psi
@Strain 3.36 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
95.4 MPa
@Strain 2.52 %, Temperature -20.0 °C
|
13800 psi
@Strain 2.52 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
117 MPa
@Strain 3.85 %, Temperature 0.000 °C
|
17000 psi
@Strain 3.85 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
133 MPa
@Strain 4.41 %, Temperature -20.0 °C
|
19300 psi
@Strain 4.41 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
3.00 MPa
@Strain 0.165 %, Time 36000 sec
|
435 psi
@Strain 0.165 %, Time 10.0 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
3.00 MPa
@Strain 0.192 %, Time 360000 sec
|
435 psi
@Strain 0.192 %, Time 100 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
3.00 MPa
@Strain 0.231 %, Time 3.60e+6 sec
|
435 psi
@Strain 0.231 %, Time 1000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
3.00 MPa
@Strain 0.146 %, Time 3600 sec
|
435 psi
@Strain 0.146 %, Time 1.00 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
3.00 MPa
@Strain 0.297 %, Time 3.60e+7 sec
|
435 psi
@Strain 0.297 %, Time 10000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
12.0 MPa
@Strain 1.45 %, Time 3.60e+7 sec
|
1740 psi
@Strain 1.45 %, Time 10000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
12.0 MPa
@Strain 0.656 %, Time 3600 sec
|
1740 psi
@Strain 0.656 %, Time 1.00 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
12.0 MPa
@Strain 1.18 %, Time 3.60e+6 sec
|
1740 psi
@Strain 1.18 %, Time 1000 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
12.0 MPa
@Strain 0.947 %, Time 360000 sec
|
1740 psi
@Strain 0.947 %, Time 100 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
12.0 MPa
@Strain 0.772 %, Time 36000 sec
|
1740 psi
@Strain 0.772 %, Time 10.0 hour
|
50%RH; isochronous; ISO 11403-1 -2 | |
抗張強度(屈服) | 67.0 MPa | 9720 psi | 50%RH; ISO 527-1/-2 |
96.0 MPa | 13900 psi | DAM; ISO 527-1/-2 | |
伸長率 (斷裂) | 13 % | 13 % | DAM; Nominal; ISO 527-1/-2 |
50 % | 50 % | 50%RH; Nominal; ISO 527-1/-2 | |
屈服伸長率 | 4.5 % | 4.5 % | DAM; ISO 527-1/-2 |
4.5 % | 4.5 % | DAM; ISO 527-3 | |
18 % | 18 % | 50%RH; ISO 527-1/-2 | |
拉伸模量 | 2.00 GPa | 290 ksi | 50%RH; ISO 527-1/-2 |
3.60 GPa | 522 ksi | DAM; ISO 527-1/-2 | |
剪切模量 | 0.175 GPa
@Temperature 160 °C
|
25.4 ksi
@Temperature 320 °F
|
DAM; Dynamic; ISO 11403-1 -2 |
0.214 GPa
@Temperature 120 °C
|
31.0 ksi
@Temperature 248 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
0.449 GPa
@Temperature 70.0 °C
|
65.1 ksi
@Temperature 158 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
1.0685 GPa
@Temperature 20.0 °C
|
154.98 ksi
@Temperature 68.0 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
1.171 GPa
@Temperature -20.0 °C
|
169.8 ksi
@Temperature -4.00 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
1.259 GPa
@Temperature -50.0 °C
|
182.6 ksi
@Temperature -58.0 °F
|
DAM; Dynamic; ISO 11403-1 -2 | |
抗剪強度 | 0.0670 MPa
@Shear Rate 500 1/s, Temperature 315 °C
|
9.72 psi
@Shear Rate 500 1/s, Temperature 599 °F
|
ISO 11403-1 -2 |
0.0975 MPa
@Shear Rate 500 1/s, Temperature 295 °C
|
14.1 psi
@Shear Rate 500 1/s, Temperature 563 °F
|
ISO 11403-1 -2 | |
0.142 MPa
@Shear Rate 500 1/s, Temperature 275 °C
|
20.6 psi
@Shear Rate 500 1/s, Temperature 527 °F
|
ISO 11403-1 -2 | |
割線模量 | 1.66 GPa
@Strain 3.84 %, Temperature 40.0 °C
|
240 ksi
@Strain 3.84 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 |
2.17 GPa
@Strain 1.92 %, Temperature 40.0 °C
|
314 ksi
@Strain 1.92 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
2.375 GPa
@Strain 0.480 %, Temperature 40.0 °C
|
344.5 ksi
@Strain 0.480 %, Temperature 104 °F
|
DAM; ISO 11403-1 -2 | |
2.52 GPa
@Strain 3.84 %, Temperature 23.0 °C
|
365 ksi
@Strain 3.84 %, Temperature 73.4 °F
|
DAM; ISO 11403-1 -2 | |
2.7381 GPa
@Strain 5.04 %, Temperature -20.0 °C
|
397.13 ksi
@Strain 5.04 %, Temperature -4.00 °F
|
DAM; ISO 11403-1 -2 | |
2.77 GPa
@Strain 4.40 %, Temperature 0.000 °C
|
402 ksi
@Strain 4.40 %, Temperature 32.0 °F
|
DAM; ISO 11403-1 -2 | |
3.41 GPa
@Strain 1.92 %, Temperature 23.0 °C
|
495 ksi
@Strain 1.92 %, Temperature 73.4 °F
|