點擊圖片查看大圖| 廠家(產(chǎn)地)：美國赫斯特 | 牌號：EC140XF-CD3068 | 加工級別：注塑級 |
| 銷售方式：品牌經(jīng)銷 | 類型：標準料 |
產(chǎn)品參數(shù)
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 密度 | ASTM D-792 | 1.54 | ||
| 物理性能 | 擴散因數(shù) | +73℉(+23℃)106Hz | ASTM D-150 | 0.009 | |
| 絕緣系數(shù) | +73℉(+23℃)102;to106Hz | ASTM D-150 | 3.1 | ||
| 電阻系數(shù) | +73℉(+23℃)0.2%H2O | ASTM D-257 | 3×1016 | ohm-cm | |
| 機械性能 | 伸張強度 | +23℃ | ASTM D-638 | 52.4 | MPa |
| 壓縮應力 | +23℃@1%Def. | ASTM D-695 | 31.0 | MPa | |
| 拉力沖擊抵抗力 | +73℉ | D1822Long | 50 | ft.lb/in2 | |
| 絕緣強度 | Short Time,90 mils | ASTM D-149 | 400(125mils) | V/mil | |
| 壓縮應力 | +73°F@1%Def. | ASTM D-695 | 4.5 | MPsi | |
| 壓縮應力 | +73°F@10%Def. | ASTM D-695 | 13.0 | MPsi | |
| 彎曲疲勞忍耐限度 | +23℃ | ASTM D-671 | 24.8 | MPa | |
| 撓曲系數(shù) | +158℉ | 在25℃下 | 190 | MPsi | |
| 撓曲系數(shù) | +73℉ | 在25℃下 | 340 | MPsi | |
| 伸張強度 | +212℉ | ASTM D-638 | 4.0 | MPsi | |
| 彎曲降服強 | +23℃ | ASTM D-790 | 72.4 | MPa | |
| Izod沖擊強度 | 40℃ | ASTM D-256 | 53.4 | j/m | |
| 彈性系數(shù) | +73℉ | ASTM D-638 | 420 | MPsi | |
| 斷裂時之拉力伸張度 | +212℉(+100℃) | ASTM D-638 | 250 | % | |
| 伸張強度 | +100℃ | ASTM D-638 | 28.3 | MPa | |
| 斷裂時之拉力伸張度 | +73℉(+23℃) | ASTM D-638 | 22 | % | |
| 拉力沖擊抵抗力 | +23℃ | D1822Long | 102 | kj/m2 | |
| 熱變形溫度 | 66psi | ASTM D-648 | 334 | ℉ | |
| 撓曲系數(shù) | +250℉ | 在25℃下 | 80 | MPsi | |
| 撓曲系數(shù) | +70℃ | 在25℃下 | 1310 | MPa | |
| 電弧抵抗力 | 120mil(3.1mm) | ASTM D-495 | 183no tracking | Sec. | |
| 洛氏硬度 | ASTM D-785 | M78,R118 | |||
| 剪力 | +73℉ | ASTM D-732 | 8.0 | MPsi | |
| 彎曲疲勞忍耐限度 | +73℉ | ASTM D-671 | 3.6 | MPsi | |
| 剪力 | +23℃ | ASTM D-732 | 55.2 | MPa | |
| 撓曲系數(shù) | -68℉ | 在25℃下 | 520 | MPsi | |
| 絕緣強度 | Short Time,2.3mm | ASTM D-149 | 15.8(3.2mm) | MV/m | |
| 伸張強度 | +250℉ | ASTM D-638 | 3.1 | MPsi | |
| 斷裂時之拉力伸張度 | -68℉(-55℃) | ASTM D-638 | 15 | % | |
| 伸張強度 | +158℉ | ASTM D-638 | 5.3 | MPsi | |
| 負載下之變形 | 2000psi@+122℉(14Mpa@50℃) | ASTM D-621 | 0.6 | % | |
| 撓曲系數(shù) | +23℃ | 在25℃下 | 2340 | MPa | |
| 撓曲系數(shù) | +122℃ | 在25℃下 | 550 | MPa | |
| 彎曲降服強 | +73℉ | ASTM D-790 | 10.5 | MPsi | |
| 伸張強度 | +122℃ | ASTM D-638 | 20.7 | MPa | |
| Izod沖擊強度 | +73℉ | ASTM D-256 | 1.2 | ft.lb/in | |
| 摩擦系數(shù) | +73℉(+23℃)動態(tài) | ThrustWasherTest3 | 0.14 | ||
| 撓曲系數(shù) | +212℉ | 在25℃下 | 110 | MPsi | |
| 斷裂時之拉力伸張度 | +158℉(+70℃) | ASTM D-638 | 50 | % | |
| 撓曲系數(shù) | +100℃ | 在25℃下 | 700 | MPa | |
| 伸張強度 | +73℉ | ASTM D-638 | 7.6 | MPsi | |
| Izod沖擊強度 | -40℉ | ASTM D-256 | 1.0 | ft.lb/in | |
| 伸張強度 | +70℃ | ASTM D-638 | 36.5 | MPa | |
| 伸張強度 | -68℉ | ASTM D-638 | 10.9 | MPsi | |
| 彈性系數(shù) | +23℃ | ASTM D-638 | 2895 | MPa | |
| 撓曲系數(shù) | -55℃ | 在25℃下 | 3585 | MPa | |
| 壓縮應力 | +23℃@10%Def. | ASTM D-695 | 89.6 | MPa | |
| 斷裂時之拉力伸張度 | +250℉(+122℃) | ASTM D-638 | >260 | % | |
| Izod沖擊強度 | +23℃ | ASTM D-256 | 64.1 | j/m | |
| 伸張強度 | -55℃ | ASTM D-638 | 75 | MPa | |
| 加工性能 | 吸水量 | 浸泡均衡點+73℉(+23℃) | ASTM D-570 | 0.72 | % |
| 吸水量 | Equil.50%R.h.+73℉(+23℃) | ASTM D-570 | 0.18 | % | |
| 吸水量 | 24hrs浸泡+73℉(+23℃) | ASTM D-570 | 0.20 | % | |
| 熱性能 | 熱變形溫度 | 0.5MPa | ASTM D-648 | 168 | ℃ |
| 熱變形溫度 | 1.8MPa | ASTM D-648 | 118 | ℃ | |
| 線性熱膨脹系數(shù) | -40 to +29℃ | ASTM D-696 | 10.4 | 10-5m/m.℃ | |
| 線性熱膨脹系數(shù) | -40 to +85℉ | ASTM D-696 | 5.8 | 10-5in/in℉ | |
| 線性熱膨脹系數(shù) | +29 to +60℃ | ASTM D-696 | 12.2 | 10-5m/m.℃ | |
| 熔點 | ASTM D-2133 | 347 | ℉ | ||
| 可燃燒性 | UL-94 | 94HB | |||
| 熱變形溫度 | 264psi | ASTM D-648 | 244 | °F | |
| 線性熱膨脹系數(shù) | +85 to +140℉ | ASTM D-696 | 6.8 | 10-5in/in℉ | |
| 熔點 | ASTM D-2133 | 175 | ℃ | ||
免責聲明：（1）以上所展示的信息由企業(yè)自行提供，內(nèi)容的真實性、準確性和合法性由發(fā)布企業(yè)負責，環(huán)球塑化網(wǎng)對此不承擔任何保證責任。我們原則上建議您優(yōu)先選擇“塑企通”會員合作! （2）同時我們鄭重提醒各位買/賣家，交易前請詳細核實對方身份，切勿隨意打款或發(fā)貨，謹防上當受騙。如發(fā)現(xiàn)虛假信息，請向環(huán)球塑化網(wǎng)舉報。